Specification for Cements and Materials for Well Cementing
ANSI/API SPECIFICATION 10A TWENTY-FOURTH EDITION, DECEMBER 2010 EFFECTIVE DATE: JUNE 1, 2011 CONTAINS API MONOGRAM ANNEX AS PART OF U.S. NATIONAL ADOPTION REAFFIRMED, APRIL 2015
ISO 10426-1:2009 (Identical), Petroleum and natural gas industries—Cements and materials for well cementing—Part 1: Specification --`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
Special Notes API publications necessarily address problems of a general nature. With respect to particular circumstances, local, state, and federal laws and regulations should be reviewed. Neither API nor any of API's employees, subcontractors, consultants, committees, or other assignees make any warranty or representation, either express or implied, with respect to the accuracy, completeness, or usefulness of the information contained herein, or assume any liability or responsibility for any use, or the results of such use, of any information or process disclosed in this publication. Neither API nor any of API's employees, subcontractors, consultants, or other assignees represent that use of this publication would not infringe upon privately owned rights. API publications may be used by anyone desiring to do so. Every effort has been made by the Institute to assure the accuracy and reliability of the data contained in them; however, the Institute makes no representation, warranty, or guarantee in connection with this publication and hereby expressly disclaims any liability or responsibility for loss or damage resulting from its use or for the violation of any authorities having jurisdiction with which this publication may conflict. API publications are published to facilitate the broad availability of proven, sound engineering and operating practices. These publications are not intended to obviate the need for applying sound engineering judgment regarding when and where these publications should be utilized. The formulation and publication of API publications is not intended in any way to inhibit anyone from using any other practices. Any manufacturer marking equipment or materials in conformance with the marking requirements of an API standard is solely responsible for complying with all the applicable requirements of that standard. API does not represent, warrant, or guarantee that such products do in fact conform to the applicable API standard.
All rights reserved. No part of this work may be reproduced, translated, stored in a retrieval system, or transmitted by any means, electronic, mechanical, photocopying, recording, or otherwise, without prior written permission from the publisher. Contact the Publisher, API Publishing Services, 1220 L Street, NW, Washington, DC 20005. Copyright © 2010 American Petroleum Institute
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API Foreword Nothing contained in any API publication is to be construed as granting any right, by implication or otherwise, for the manufacture, sale, or use of any method, apparatus, or product covered by letters patent. Neither should anything contained in the publication be construed as insuring anyone against liability for infringement of letters patent. Shall: As used in a standard, “shall” denotes a minimum requirement in order to conform to the specification. Should: As used in a standard, “should” denotes a recommendation or that which is advised but not required in order to conform to the specification. This document was produced under API standardization procedures that ensure appropriate notification and participation in the developmental process and is designated as an API standard. Questions concerning the interpretation of the content of this publication or comments and questions concerning the procedures under which this publication was developed should be directed in writing to the Director of Standards, American Petroleum Institute, 1220 L Street, NW, Washington, DC 20005. Requests for permission to reproduce or translate all or any part of the material published herein should also be addressed to the director. Generally, API standards are reviewed and revised, reaffirmed, or withdrawn at least every five years. A one-time extension of up to two years may be added to this review cycle. Status of the publication can be ascertained from the API Standards Department, telephone (202) 682-8000. A catalog of API publications and materials is published annually by API, 1220 L Street, NW, Washington, DC 20005. This standard shall become effective on the date printed on the cover but may be used voluntarily from the date of distribution. Standards referenced herein may be replaced by other international or national standards that can be shown to meet or exceed the requirements of the referenced standard. Suggested revisions are invited and should be submitted to the Standards Department, API, 1220 L Street, NW, Washington, DC 20005,
[email protected]. This American National Standard is under the jurisdiction of the API Subcommittee 10 on Well Cements. This standard is considered identical to the English version of ISO 10426-1. ISO 10426-1 was prepared by Technical Committee ISO/TC 67, Subcommittee 3 on Drilling and completion fluids, and well cements. This identical version includes ISO 10426-1 Technical Corrigendum, 2010. In this American National Standard, the following editorial changes have been made in the document: Annex B is regional annex added for API Monogram licensees.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
This standard replaces API Specification 10A, 23rd edition.
iii Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
Contents
Page
Foreword ............................................................................................................................................................ vi Introduction ....................................................................................................................................................... vii
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
1
Scope ...................................................................................................................................................... 1
2
Normative references ............................................................................................................................ 1
3
Terms and definitions ........................................................................................................................... 2
4 4.1 4.2
Requirements......................................................................................................................................... 3 Specification, chemical and physical requirements .......................................................................... 3 Sampling frequency, timing of tests, and equipment ........................................................................ 7
5
Sampling procedure .............................................................................................................................. 8
6 6.1 6.2
Fineness tests........................................................................................................................................ 8 Procedure ............................................................................................................................................... 8 Requirements......................................................................................................................................... 8
7 7.1 7.2
Preparation of slurry for free-fluid, compressive strength and thickening-time tests .................. 8 Apparatus ............................................................................................................................................... 8 Procedure ............................................................................................................................................. 10
8 8.1 8.2 8.3 8.4 8.5
Free-fluid test (formerly free water) ................................................................................................... 11 Apparatus ............................................................................................................................................. 11 Calibration ............................................................................................................................................ 15 Procedure ............................................................................................................................................. 16 Calculation of percent free fluid ........................................................................................................ 16 Acceptance requirements .................................................................................................................. 17
9 9.1 9.2 9.3 9.4
Compressive strength tests ............................................................................................................... 17 Apparatus ............................................................................................................................................. 17 Procedure ............................................................................................................................................. 18 Test procedure (after ASTM C109/C109M) ........................................................................................ 20 Compressive strength acceptance criteria ....................................................................................... 20
10 10.1 10.2 10.3 10.4 10.5
Thickening-time tests.......................................................................................................................... 21 Apparatus ............................................................................................................................................. 21 Calibration ............................................................................................................................................ 27 Procedure ............................................................................................................................................. 29 Thickening time and consistency ...................................................................................................... 31 Specification acceptance requirements............................................................................................ 31
11
Marking ................................................................................................................................................. 32
12
Packing ................................................................................................................................................. 32
13
Bentonite .............................................................................................................................................. 32
Annex A (informative) Calibration procedures for thermocouples, temperature measuring systems, and controllers..................................................................................................................................... 33 Annex B (informative) Use of the API Monogram by Licensees ................................................................ 35 Bibliography ...................................................................................................................................................... 38
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
v Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
ISO 10426-1 was prepared by Technical Committee ISO/TC 67, Materials, equipment and offshore structures for petroleum, petrochemical and natural gas industries, Subcommittee SC 3, Drilling and completion fluids, and well cements. This third edition cancels and replaces the second edition (ISO 10426-1:2005), which has been technically revised. ISO 10426 consists of the following parts, under the general title Petroleum and natural gas industries — Cements and materials for well cementing: ⎯ Part 1: Specification ⎯ Part 2:Testing of well cements ⎯ Part 3: Testing of deepwater well cement formulations ⎯
Part 4: Preparation and testing of foamed cement slurries at atmospheric pressure
⎯ Part 5: Determination of shrinkage and expansion of well cement formulations at atmospheric pressure ⎯ Part 6: Methods for determining the static gel strength of cement formulations
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
vi Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights.
Introduction This part of ISO 10426 is based on ISO 10426-1:2005 with the intent that the 24th edition of API Spec 10A will be identical to this part of ISO 10426. It is necessary that users of this part of ISO 10426 be aware that further or differing requirements can be required for individual applications. This part of ISO 10426 is not intended to inhibit a vendor from offering, or the purchaser from accepting, alternative equipment or engineering solutions for the individual application. This can be particularly applicable where there is innovative or developing technology. Where an alternative is offered, it is the responsibility of the vendor to identify any variations from this part of ISO 10426 and provide details. In this part of ISO 10426, where practical, US Customary (USC) or other units are included in brackets for information. The units do not necessarily represent a direct conversion of SI to USC units, or USC to SI. Consideration has been given to the precision of the instrument making the measurement. For example, thermometers are typically marked in 1° increments, thus temperature values have been rounded to the nearest degree. In this part of ISO 10426, calibrating an instrument refers to assuring the accuracy of the measurement. Accuracy is the degree of conformity of a measurement of a quantity to its actual or true value. Accuracy is related to precision, or reproducibility, of a measurement. Precision is the degree to which further measurements or calculations will show the same or similar results. Precision is characterized in terms of the standard deviation of the measurement. The results of calculations or a measurement can be accurate, but not precise, precise but not accurate, neither or both. A result is valid if it is both accurate and precise.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
vii Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API Specification 10A/ISO 10426-1
Petroleum and natural gas industries – Cements and materials for well cementing Part 1: Specification 1
Scope
This part of ISO 10426 specifies requirements and gives recommendations for six classes of well cements, including their chemical and physical requirements and procedures for physical testing. This part of ISO 10426 is applicable to well cement classes A, B, C and D, which are the products obtained by grinding Portland cement clinker and, if needed, calcium sulfate as an interground additive. Processing additives can be used in the manufacture of cement of these classes. Suitable set-modifying agents can be interground or blended during manufacture of class D cement. This part of ISO 10426 is also applicable to well cement classes G and H, which are the products obtained by grinding clinker with no additives other than one or more forms of calcium sulfate, water or chemical additives as required for chromium (VI) reduction.
2
Normative references
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 3310-1, Test sieves — Technical requirements and testing — Part 1: Test sieves of metal wire cloth ISO 13500, Petroleum and natural gas industries — Drilling fluid materials — Specifications and tests ISO 24450, Laboratory glassware — Wide-necked boiling flasks ASTM C109/C109M, Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens) ASTM C114, Standard Test Methods for Chemical Analysis of Hydraulic Cement ASTM C115, Standard Test Method for Fineness of Portland Cement by the Turbidimeter
ASTM C204, Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus ASTM C465, Standard Specification for Processing Additions for Use in the Manufacture of Hydraulic Cements ASTM E11, Standard Specification for Wire Cloth and Sieves for Testing Purposes ASTM E1404-94(2008), Standard Specification for Laboratory Glass Conical Flasks Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for1 Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
ASTM C183, Standard Practice for Sampling and the Amount of Testing of Hydraulic Cement
2
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
EN 196-1, Methods of testing cement — Part 1: Determination of strength EN 196-2, Methods of testing cement — Part 2: Chemical analysis of cement EN 196-6, Methods of testing cement — Part 6: Determination of fineness EN 196-7, Methods of testing cement — Part 7: Methods of taking and preparing samples of cement
3
Terms and definitions
For the purposes of this document, the following terms and definitions apply. 3.1 additive material added to a cement slurry to modify or enhance some desired property NOTE Properties that are commonly modified include setting time (by use of retarders or accelerators), fluid loss, viscosity, etc.
3.2 atmospheric pressure consistometer device used for stirring and conditioning the cement slurry NOTE
The device is not intended to measure thickening time.
3.3 Bearden unit of consistency Bc measure of the consistency of a cement slurry when determined on a pressurized consistometer
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
3.4 cement Portland cement ground clinker generally consisting of hydraulic calcium silicates and aluminates and usually containing one or more forms of calcium sulfate as an interground additive 3.5 cement class designation achieved under the ISO system for classification of well cement according to its intended use 3.6 cement grade designation achieved under the ISO system for denoting the sulfate resistance of a particular cement 3.7 cement blend mixture of dry cement and other dry materials 3.8 clinker fused materials produced in the kiln during cement manufacturing that are interground with calcium sulfate to make cement Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
3
3.9 compressive strength force per unit area required to cause a set cement sample to fail under compression 3.10 consistometer device used to measure the thickening time of a cement slurry under temperature and under pressure 3.11 filtrate liquid that is forced out of a cement slurry during a fluid loss test 3.12 free fluid coloured or colourless liquid that separates from a cement slurry under static conditions
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
3.13 slurry container slurry cup container in an atmospheric or pressurized consistometer used to hold the slurry for conditioning purposes or for the thickening-time test 3.14 thickening time time after which the consistency of a cement slurry has become so high that the slurry is considered unpumpable
NOTE The results of a thickening-time test provide an indication of the length of time a cement slurry remains pumpable under the test conditions.
4
Requirements
4.1
Specification, chemical and physical requirements
4.1.1 4.1.1.1
Classes and grades General
Well cement shall be specified using classes A, B, C, D, G and H and the grades: ordinary (O), moderate sulfateresistant (MSR) and high sulfate-resistant (HSR). A well cement that has been manufactured and supplied in accordance with this part of ISO 10426 may be mixed and placed in the field using water ratios or additives at the user's discretion. It is not intended that manufacturing compliance with this part of ISO 10426 be based on such field conditions. Processing additives, set modifying agents or chemical additives used to reduce chromium (VI) shall not prevent a well cement from performing its intended functions. 4.1.1.2
Class A
This product is obtained by grinding clinker, consisting essentially of hydraulic calcium silicates, usually containing one or more forms of calcium sulfate as an interground additive. At the option of the manufacturer, processing additives may be used in the manufacture of class A cement, provided that such materials in the amounts used have been shown to meet the requirements of ASTM C465. This product is intended for use when special properties are not required and is available only in O grade, similar to ASTM C150, type I. Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
4
4.1.1.3
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Class B
This product is obtained by grinding clinker, consisting essentially of hydraulic calcium silicates, usually containing one or more forms of calcium sulfate as an interground additive. At the option of the manufacturer, processing additives may be used in the manufacture of class B cement, provided that such materials in the amounts used have been shown to meet the requirements of ASTM C465. This product is intended for use when conditions require moderate or high sulfate resistance and is available in both MSR and HSR grades, similar to ASTM C150, type II. 4.1.1.4
Class C
This product is obtained by grinding clinker, consisting essentially of hydraulic calcium silicates, usually containing one or more forms of calcium sulfate as an interground additive. At the option of the manufacturer, processing additives may be used in the manufacture of class C cement, provided that such materials in the amounts used have been shown to meet the requirements of ASTM C465. This product is intended for use when conditions require high, early strength and is available in O, MSR and HSR grades, similar to ASTM C150, type III. 4.1.1.5
Class D
This product is obtained by grinding clinker, consisting essentially of hydraulic calcium silicates, usually containing one or more forms of calcium sulfate as an interground additive. At the option of the manufacturer, processing additives may be used in the manufacture of class D cement, provided that such materials in the amounts used have been shown to meet the requirements of ASTM C465. Further, at the option of the manufacturer, suitable set-modifying agents may be interground or blended during manufacture. This product is intended for use under conditions of moderately high temperatures and pressures and is available in MSR and HSR grades. 4.1.1.6
Class G
This product is obtained by grinding clinker, consisting essentially of hydraulic calcium silicates, usually containing one or more forms of calcium sulfate as an interground additive. No additives other than calcium sulfate or water, or both, shall be interground or blended with the clinker during manufacture of class G well cement. Chemical additives, as required for chromium(VI) reduction, are permitted, provided that such additives do not prevent the well cement from performing its intended purpose. This product is intended for use as a basic well cement and is available in MSR and HSR grades. 4.1.1.7
Class H
This product is obtained by grinding clinker, consisting essentially of hydraulic calcium silicates, usually containing one or more forms of calcium sulfate as an interground additive. No additives other than calcium sulfate or water, or both, shall be interground or blended with the clinker during manufacture of class H well cement. Chemical additives, as required for chromium(VI) reduction, are permitted, provided that such additives do not prevent the well cement from performing its intended purpose. This product is intended for use as a basic well cement and is available in MSR and HSR grades. 4.1.2
Chemical requirements
Well cements shall conform to the respective chemical requirements of classes and grades referenced in Table 1. It is not intended that this manufacturing compliance be applicable to field conditions. This part of ISO 10426 is not applicable to the use of cements that do not conform to the chemical requirements of classes and grades as set forth in Table 1. Chemical analyses of hydraulic cements shall be carried out as specified in EN 196-2. NOTE
For the purposes of this provision, ASTM C114 is equivalent to EN 196-2. --`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
5
Table 1 — Chemical requirements Cement class A
B
C
D
G
H
6,0
NAa
6,0
NA
NA
NA
Ordinary grade (O) Magnesium oxide (MgO), maximum, percent Sulfur trioxide (SO3), maximum,
percentb
3,5
NA
4,5
NA
NA
NA
Loss on ignition, maximum, percent
3,0
NA
3,0
NA
NA
NA
Insoluble residue, maximum, percent
0,75
NA
0,75
NA
NA
NA
Tricalcium aluminate (C3A), maximum, percentd
NRc
NA
15
NA
NA
NA
Magnesium oxide (MgO), maximum, percent
NA
6,0
6,0
6,0
6,0
6,0
Sulfur trioxide (SO3), maximum, percentb
NA
3,0
3,5
3,0
3,0
3,0
Loss on ignition, maximum, percent
NA
3,0
3,0
3,0
3,0
3,0
Insoluble residue, maximum, percent
NA
0,75
0,75
0,75
0,75
0,75
Tricalcium silicate (C3S) maximum, percentd
NA
NR
NR
NR
58
58
minimum, percentd
NA
NR
NR
NR
48
48
NA
8
8
8
8
8
NA
NR
NR
NR
0,75
0,75
Magnesium oxide (MgO), maximum, percent
NA
6,0
6,0
6,0
6,0
6,0
Sulfur trioxide (SO3), maximum, percentb
NA
3,0
3,5
3,0
3,0
3,0
Tricalcium aluminate (C3A), maximum percentd Total alkali content, expressed as sodium oxide (Na2O) equivalent, maximum, percente High sulfate-resistant grade (HSR)
Loss on ignition, maximum, percent
NA
3,0
3,0
3,0
3,0
3,0
Insoluble residue, maximum, percent
NA
0,75
0,75
0,75
0,75
0,75
Tricalcium silicate (C3S) maximum, percentd
NA
NR
NR
NR
65
65
NA
NR
NR
NR
48
48
Tricalcium aluminate (C3A), maximum, percentd
NA
3
3
3
3
3
Tetracalcium aluminoferrite (C4AF) plus twice the tricalcium aluminate (C3A), maximum, percentd
NA
24
24
24
24
24
Total alkali content expressed as sodium oxide (Na2O) equivalent, maximum, percente
NA
NR
NR
NR
0,75
0,75
minimum, percentd
a
NA indicates “not applicable”.
b
When the tricalcium aluminate content (expressed as C3A) of the cement is 8 % or less, the maximum SO3 content shall be 3 %, or 3,5 % for class C cement. c
NR indicates “no requirement”.
d
The expressing of chemical limitations by means of calculated assumed compounds does not necessarily mean that the oxides are actually or entirely present as such compounds. The compounds are calculated according to the ratio of the mass percentages of Al2O3 to Fe2O3, where w is the percentage mass fraction of the compound indicated in the subscript: —
When wAl O /wFe O is greater than 0,64, the compounds shall be calculated as follows: 2 3 2 3 C3A = 2,65wAl O − 1,69wFe O 2 3 2 3 C3S = 4,07wCaO − 7,60wSiO − 6,72wAl O − 1,43wFe O − 2,85wSO 2 2 3 2 3 3 C4AF = 3,04wFe O 2 3
—
When wAl O /wFe O is 0,64 or less, the C3A content is zero. 2 3 2 3
—
The C3S and C4AF shall be calculated as follows: C3S = 4,07wCaO − 7,60wSiO − 4,48wAl O − 2,86wFe O − 2,85wSO 2 2 3 2 3 3
e
C4AF = 3,04wFe O 2 3 The sodium oxide equivalent, expressed as Na2O equivalent, shall be calculated by the formula: Na2O equivalent is equal to 0,658wK O + wNa O. 2 2
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Moderate sulfate-resistant grade (MSR)
6
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
4.1.3
Physical and performance requirements
Well cement shall conform to the respective physical and performance requirements specified in Table 2 and in Clauses 6 through 10. Table 2 — Summary of physical and performance requirements Well cement class
A
B
C
D
G
H
46
46
56
38
44
38
Turbidimeter (specific surface, minimum, m2/kg)
150
160
220
NRa
NR
NR
Air permeability (specific surface, minimum, m2/kg)
280
280
400
NR
NR
NR
NR
NR
NR
NR
5,9
5,9
Mix water, % mass fraction of cement (Table 5) Fineness tests (alternative methods) (Clause 6)
Free-fluid content, maximum, percent (Clause 8) Compressive strength test (8 h curing time)
Schedule number Table 6
Final curing temperature °C (°F)
Curing pressure MPa (psi)
(Clause 9)
NAb
38 (100)
atm.
1,7 (250)
1,4 (200)
2,1 (300)
NR
2,1 (300)
2,1 (300)
(Clause 9)
NA
60 (140)
atm.
NR
NR
NR
NR
10,3 (1 500)
10,3 (1 500)
(Clause 9)
6S
110 (230)
20,7 (3 000)
NR
NR
NR
3,4 (500)
NR
NR
Compressive strength test (24 h curing time)
Schedule number (Table 6)
Final curing temperature °C (°F)
Curing pressure MPa (psi)
(Clause 9)
NA
38 (100)
atm.
12,4 (1 800)
10,3 (1 500)
13,8 (2 000)
NR
NR
NR
(Clause 9)
4S
77 (170)
20,7 (3 000)
NR
NR
NR
6,9 (1 000)
NR
NR
(Clause 9)
6S
110 (230)
20,7 (3 000)
NR
NR
NR
13,8 (2 000)
NR
NR
Thickeningtime test
Specification test schedule number Tables 9 through 11
Maximum consistency (15 min to 30 min stirring period) Bcc
(Clause 10)
4
30
90d
90d
90d
90d
NR
NR
(Clause 10)
5
30
NR
NR
NR
NR
90d
90d
(Clause 10)
5
30
NR
NR
NR
NR
120e
120e
(Clause 10)
6
30
NR
NR
NR
100d
NR
NR
a
NR indicates “no requirement”.
b
NA indicates “not applicable”.
Minimum compressive strength MPa (psi)
Minimum compressive strength MPa (psi)
Thickening time (minimum/maximum) min
c
Bearden units of consistency, Bc, obtained on a pressurized consistometer as defined in Clause 10 and calibrated in accordance with the same clause.
d
Minimum thickening time.
e
Maximum thickening time.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
4.2
7
Sampling frequency, timing of tests, and equipment
4.2.1
Sampling frequency
4.2.1.1 For well cement classes C, D, G, and H, a sample for testing shall be taken by either of the following methods: a)
over an interval of 24 h;
b)
on a 1 000 ton (maximum) production run.
4.2.1.2 For well cement classes A and B, a sample for testing shall be taken by either of the following methods: a)
over a 14-day interval;
b)
on a 25 000 ton (maximum) production run.
4.2.1.3 These samples shall represent the product as produced. At the choice of the manufacturer, either sampling method may be used. 4.2.2
Time from sampling to testing
Each sample shall be tested for conformance to this part of ISO 10426. All tests shall be completed within seven working days after sampling. 4.2.3
Specified equipment
Equipment used for testing well cements shall comply with Table 3. Dimensions shown in Figures 5 through 7 and Figures 10 through 12 are for the purposes of manufacturing the cement-specification test equipment. Dimensional recertification is not required. 4.2.4
Calibration
Equipment calibrated in accordance with the requirements of this part of ISO 10426 is considered accurate if the calibration is within the specified limits. Table 3 — Specification test equipment for well-cement manufacturers Test or preparation Sampling
Well cement classes
Clause reference
All
5
Required equipment Apparatus as specified in EN 196-7 NOTE For the purposes of this provision, ASTM C183 is equivalent to EN 196-7.
Fineness
A, B, C
6
Turbidimeter and auxiliary equipment as specified in ASTM C115 or air permeability apparatus and auxiliary equipment as specified in EN 196-6. NOTE For the purposes of this provision, ASTM C204 is equivalent to EN 196-6.
Slurry preparation
All
7
Apparatus as specified in 7.1
G, H
8
Apparatus as specified in 8.1
Atmospheric pressure compressive strength
A, B, C, G, H
9
Apparatus as specified in 9.1
Pressure cured compressive strength
D
9
Apparatus as specified in 9.1, except pressurized curing bath of 9.1.3.3
Thickening time
All
10
Pressurized consistometer specified in 10.1
Free fluid
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`--
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
8
5
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Sampling procedure
One or more of the procedures in accordance with EN 196-7 shall be used to secure a sample of well cement for specification testing purposes. NOTE
6
For the purposes of this provision, ASTM C183 is equivalent to EN 196-7.
Fineness tests
6.1
Procedure
Tests for fineness of well cement shall be carried out in accordance with either the procedure in ASTM C115 for the turbidimeter test or the procedure in EN 196-6 by air permeability apparatus for the air permeability test. NOTE
6.2
For the purposes of this provision, ASTM C204 is equivalent to EN 196-6.
Requirements
Acceptance requirements for the fineness test are a minimum specific surface area (expressed in square metres per kilogram) as given in Table 2. Classes D, G and H cements have no fineness requirement. At the discretion of the manufacturer, either of the two fineness test methods (turbidimeter or air permeability test) shall be used to determine the fineness.
7
Preparation of slurry for free-fluid, compressive strength and thickening-time tests
7.1 7.1.1
Apparatus Scales
The indicated load on scales shall be accurate within 0.1% of the actual load, unless measurements are being made between 0.1g to 10 g for which the indicated load shall be within 0.01g of the actual load. Annual calibration is required. 7.1.2
Mass of reference weights
The mass of the reference weights shall be accurate to within the tolerance shown in Table 4. On beam-type scales where the reference weights are on the beam, the indicated masses shall conform to the requirements given in 7.1.1. Table 4 — Permissible variation in mass of reference weights Mass g
Permissible variation g
1 000
± 1,00
500
± 0,50
300
± 0,30
200
± 0,20
100
± 0,10
50
± 0,05
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
7.1.3
9
Sieves
A No. 20 wire cloth sieve (openings 850 µm), in accordance with the requirements given in ISO 3310-1, shall be used for sieving cement prior to slurry preparation. NOTE
7.1.4
For the purposes of this provision, ASTM E11 is equivalent to ISO 3310-1.
Mixing devices
The mixing device for the preparation of well cement slurries shall be a 1 l (1 qt) size, bottom-drive, blade-type mixer. An example of a mixing device in common use is shown in Figure 1. The mixing-blade assembly and mixing container shall be constructed of durable, corrosion-resistant material. The mixing-blade assembly (see Figure 2) shall be constructed in such a manner that the blade can be removed for weighing and changing. The mixing blade shall be weighed initially and thereafter periodically, and replaced with an unused blade before a 10 % mass loss has occurred. Replace the blade if obvious blade deformation has occurred. If the mixing device leaks at any time during the mixing procedure, the contents shall be discarded, the leak shall be repaired and the procedure shall be restarted. The mixing device shall be calibrated annually to a tolerance of ± 200 r/min (± 3,3 r/s) at 4 000 r/min (66,7 r/s) rotational speed, and ± 500 r/min (± 8,3 r/s) at 12 000 r/min (200 r/s) rotational speed.
Figure 1 — Example of a typical cement-mixing device
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
10
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Figure 2 — Mixing-blade assembly
7.2 7.2.1
Procedure Sieving
Prior to mixing, the cement shall be sieved using the method described in EN 196-7 using a sieve defined in 7.1.3. NOTE
7.2.2
For the purposes of this provision, ASTM C183 is equivalent to EN 196-7.
Temperature of water and cement
The temperature of the mix water in the container within 60 s prior to mixing shall be 23 °C ± 1 °C (73 °F ± 2 °F) and the temperature of the cement within 60 s prior to mixing shall be 23 °C ± 1 °C (73 °F ± 2 °F). 7.2.3
Mix water
Distilled or de-ionized water shall be used for testing. The mix water shall be weighed directly into a clean, dry mixing container. No water shall be added to compensate for evaporation, wetting, etc. 7.2.4
Mixing quantities
The quantities of slurry component shown in Table 5 shall be used for testing. The use of the quantities of components shown in Table 5 results in mix-water percentages (based on the mass of dry cement) consistent with water percentages shown in Table 2. Table 5 — Slurry requirements
7.2.5
Components
Classes A and B g
Class C g
Classes D and H g
Class G g
Mix water
355 ± 0,5
383 ± 0,5
327 ± 0,5
349 ± 0,5
Cement
772 ± 0,5
684 ± 0,5
860 ± 0,5
792 ± 0,5
Mixing cement and water
The mixing container with the required mass of mix water, as specified in Table 5, shall be placed on the mixer base, the motor turned on and maintained at 4 000 r/min ± 200 r/min (66,7 r/s ± 3,3 r/s) while the cement sample is added at a uniform rate during no more than 15 s. After 15 s at 4 000 r/min ± 200 r/min (66,7 r/s ± 3,3 r/s), place the cover on the mixing container and continue mixing at 12 000 r/min ± 500 r/min (200 r/s ± 8,3 r/s) for 35 s ±1 s.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
8
11
Free-fluid test (formerly free water)
8.1
Apparatus
8.1.1
Consistometer
The atmospheric pressure consistometer or the pressurized consistometer described in 10.1 (run at atmospheric pressure) shall be used for stirring and conditioning the cement slurry for the determination of free-fluid content. The atmospheric consistometer consists of a rotating cylindrical slurry container, equipped with an essentially stationary paddle assembly, in a temperature-controlled liquid bath. It shall be capable of maintaining the temperature of the bath at 27 °C ± 2 °C (80 °F ± 3 °F) and of rotating the slurry container at a speed of 150 r/min ±15 r/min (2,5 r/s ± 0,25 r/s) during the stirring and conditioning period for the slurry. The paddle and all parts of the slurry container exposed to the slurry shall be constructed of corrosion-resistant materials. See Figures 3 through 6.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Key 1 2 3 4
lid (see Figure 4) fill indicating groove slurry container (see Figure 5) paddle (see Figure 6)
Figure 3 — Typical container assembly for an atmospheric pressure consistometer Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
12
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Key 1 2 3 4 5 6
cap lock nut centre lock reverse jam nut dial pointer dial and base assembly spring
7 8 9 10 11 12
collar bearing retaining ring lid roll pin shaft
Figure 4 — Typical lid and mechanism for an atmospheric pressure consistometer
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
13
Dimensions in millimetres (inches) unless otherwise indicated
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Key 1 2 3 4
two slots 180° apart fill-level indicating groove pivot bearing opposite side
a
Typical.
Figure 5 — Typical container for an atmospheric pressure consistometer Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
14
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Dimensions in millimetres (inches) unless otherwise indicated
a
Paddle material is 300 series stainless steel 1,0 mm × 7,9 mm (0,04 in × 0,311 in).
b
Shaft material is 400 series steel 6,4 mm × 211,1 mm (0,25 in × 8,311 in) annealed and ground.
c
Typical.
Figure 6 — Typical paddle for an atmospheric pressure consistometer --`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
8.1.2
15
Scales
Scales shall meet the requirements set in 7.1.1. 8.1.3
Test flask
A 500 ml conical flask, in accordance with ASTM E1404-94(2008), type I, class 2, or with ISO 24450 shall be used. See Figure 7. Dimensions in millimetres
a b
Wall thickness. Outside diameter (at widest point).
Figure 7 — The ASTM conical flask for free-fluid measurement
8.2 8.2.1
Calibration Temperature measuring system
Temperature-measuring and -controlling devices shall be calibrated no less frequently than quarterly. This includes thermometers, thermocouples and temperature controllers on consistometers, curing chambers and ultrasonic devices, and those that are used separate from or are not an integral part of the instrument. Measurements shall be made at no fewer than three temperatures spanning the manufacturer- or user-defined operating range of the equipment on or with which the device is used. The lowest temperature calibrated shall be no more than 5 °C (10 °F) above the minimum and the highest temperature calibrated shall be no more than 5 °C (10 °F) below the maximum of the user-defined operating range of the instrument. Thermometers or thermocouples shall be calibrated by the use of a known temperature source (such as a heat block) with a thermometer or thermocouple that is certified and traceable to a national standardization body. Accuracy shall be within 2 °C (3 °F). If the error in the thermometer or thermocouple is greater than that, it shall be replaced by one meeting the accuracy requirements. Thermocouples mounted in the cylinder wall of a consistometer, if not used for controlling the temperature in the consistometer, are exempt from calibration. More detailed information can be found in Annex A. 8.2.2
Slurry container rotational speed
The rotational speed shall be 150 r/min ± 15 r/min (2,5 r/s ± 0,25 r/s). The rotational speed of the slurry container shall be checked no less frequently than quarterly, and corrected if found to be outside this range.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
16
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
8.2.3
Timer
The timer shall be accurate to within ± 30 s per hour. It shall be checked for accuracy no less frequently than annually, and corrected or replaced if found to be less accurate.
8.3
Procedure
8.3.1
Prepare the slurry in accordance with the procedure in Clause 7.
8.3.2
Fill a clean and dry consistometer slurry container to the fill groove.
8.3.3 Assemble the slurry container and associated parts, place them in the consistometer and start the motor according to the operating instructions of the manufacturer. The interval between completion of mixing and starting of the consistometer shall not exceed 1 min. 8.3.4 Stir the slurry in the consistometer for a period of 20 min ± 30 s. Maintain the temperature of the slurry at 27 °C ± 2 °C (80°F ± 3 °F) and atmospheric pressure throughout the stirring period. 8.3.5 Transfer 790 g ± 5 g of class H slurry or 760 g ± 5 g of class G slurry directly into the clean, dry 500 ml conical flask within 1 min of the end of stirring. Record the actual mass transferred. Seal the flask to prevent evaporation. 8.3.6 Set the slurry-filled flask on a surface that is nominally level and vibration-free. The laboratory air temperature to which the slurry-filled flask is exposed shall be 23 °C ± 3 °C (73 °F ± 6 °F). The temperature sensor for measuring air temperature shall meet the requirements of 8.2.1. Let the slurry-filled flask remain undisturbed for a period of 2 h ± 5 min. 8.3.7 At the end of the 2 h ± 5 min period, remove the supernatant fluid that has developed with a pipette or syringe. Measure the volume of supernatant fluid to an accuracy of ± 0,1 ml and record it as “millilitres free fluid.” 8.3.8 Convert the millilitres free fluid to a percentage of starting slurry volume (∼400 ml depending on the recorded initial mass) and express that value as percent free fluid.
8.4
Calculation of percent free fluid
The volume fraction, ϕ, of free fluid in the slurry, expressed as a percentage, is then calculated using Equation (1):
ϕ=
VFF ⋅ ρ × 100 mS
(1)
where VFF
is the volume of free fluid (supernatant fluid) collected, expressed in millilitres;
ρ
is the specific gravity of slurry, equal to 1,98 for class H at 38 % water and 1,91 for class G at 44 % water; if the specific gravity of the base cement is other than the typical value of 3,18 ± 0,04, the actual specific gravity of slurry should be calculated and used;
mS
is the initially recorded (starting) mass of the slurry, expressed in grams.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
EXAMPLE
17
Calculation of percent free fluid:
mS = 791,7 g VFF = 15,1 ml
ρ = 1,98 g/cm3 (class H) ϕ = 15,1 × (1,98) × 100/791,7 ϕ = 3,78 NOTE
8.5
Millilitres and cubic centimetres are assumed to be equal for purposes of calculation.
Acceptance requirements
The free fluid for classes G and H well cements shall not exceed 5,9 %.
9
Compressive strength tests
9.1
Apparatus
9.1.1
Cube moulds and compressive strength-testing machine
Moulds and testing machine for compressive strength tests shall conform to the requirements in ASTM C109/C109M or EN 196-1, except for a)
the bearing block surface dimension requirement;
b)
the bearing block Rockwell hardness requirement;
c)
the moulds, which may be separable into more than two parts.
The moulds shall be checked for tolerances at least once every two years. The load frame used to measure the break force of cement specimens shall be calibrated no less frequently than annually. Indicated force shall deviate by no more than 2 % of the applied load or one minimum instrument scale division, whichever is greater, at 9,0 kN (2 000 lbf) load and at a minimum of 25 %, 50 % and 75 % of the range of the load cell or load indicator. With units having multiple indicators for different ranges, each indicator shall be calibrated according to these criteria. 9.1.2
Cube mould base and cover plates
Generally, plate glass, brass or stainless steel plates having a minimum thickness of 6 mm (1/4 in) are used. Cover plates may be grooved on the surface that contacts the top of the cement. 9.1.3 9.1.3.1
Water curing bath General
A curing bath or tank having dimensions that allow the complete immersion of a compressive strength mould(s) in water and capable of maintaining the prescribed test temperatures within ± 2 °C (± 3 °F) shall be employed. The two types of water curing baths are described in 9.1.3.2 and 9.1.3.3. 9.1.3.2
Atmospheric pressure curing bath
An atmospheric pressure curing bath is a vessel for curing specimens at atmospheric pressure and temperatures of 66 °C (150 °F) or less, having an agitator or circulating system.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
18
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
9.1.3.3
Pressurized curing bath
A pressurized curing bath is a vessel suitable for curing specimens at temperatures up to 110 °C (230 °F) and under pressure that can be controlled at 20,7 MPa ± 3,45 MPa (3 000 psi ± 500 psi). The vessel shall be capable of fulfilling the appropriate specification schedule given in Table 6. 9.1.4
Cooling bath
The cooling bath dimensions shall be such that the specimens being cooled from the curing temperature can be completely submerged in water maintained at 27 °C ± 3 °C (80 °F ± 6 °F). 9.1.5
Temperature-measuring system
9.1.5.1
General
The temperature-measuring system shall be calibrated to an accuracy of ± 2 °C (± 3 °F) no less frequently than quarterly. The procedure described in Annex A is commonly used. Two commonly used temperature-measuring systems are described in 9.1.5.2 and 9.1.5.3. 9.1.5.2
Thermometer
A thermometer with a range from 21 °C to 82 °C (70 °F to 180 °F), with minimum scale divisions not exceeding 1 °C (2 °F) may be used. Thermocouple
A thermocouple system with the appropriate range may be used. 9.1.6
Puddling rod
A corrosion-resistant puddling rod of nominal diameter 6 mm (1/4 in) is typically used. 9.1.7
Sealant
A sealant having a consistency that permits ease of use, good sealing properties to prevent leakage, water resistance, inertness to the cement, and is non-corrosive when subjected to the curing temperatures and pressures specified in Table 7, is commonly used to seal the exterior contact points of the specimen mould.
9.2
Procedure
9.2.1
Preparation of moulds
The base of assembled moulds shall be watertight. The interior faces of the moulds and the contact surfaces of the plates shall be clean and dry, and they may be lightly coated with release agent. 9.2.2 9.2.2.1
Preparation and placement of slurry Slurry
Prepare the cement slurry in accordance with Clause 7. 9.2.2.2
Placing slurry in moulds
Place the slurry in the prepared moulds in a layer approximately one-half of the mould depth. Use the puddling rod to puddle the slurry in an evenly distributed pattern, 27 times per specimen. Place the slurry in all the specimen compartments before commencing the puddling operation. After puddling the layer, stir the remaining slurry by hand, using a puddling rod or spatula to minimize segregation. Fill the moulds to overflowing and puddle the same as for the first layer. After puddling, use a straight-edge to strike off the excess slurry level with the top of the mould. Discard specimens in moulds that leak. Place a clean, dry cover plate on top of the mould. No less than three specimens shall be used for each test determination.
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
9.1.5.3
API SPECIFICATION 10A/ISO 10426-1
9.2.2.3
19
Pressure and temperature schedules
For classes A, B, C, G and H cements, place the specimens in the water bath preheated to the final curing temperature for tests at atmospheric pressure, within 5 min after mixing (see Table 2). For class D cement, place the specimens in the pressure vessel in water at 27 °C ± 3 °C (80 °F ± 6 °F), and within 5 min after mixing, apply temperature and pressure according to Table 6. Table 6 — Specification schedules for pressurized curing of specimens Schedule number
4S 6S
Curing pressurea MPa (psi)
20,7 (3 000) 20,7 (3 000)
0:00
Elapsed time from first application of heat and pressure h: min (± 2 min) 0:30 0:45 1:00 1:15 1:30 2:00 2:30 3:00 3:30 Temperature °C (°F)
4:00
27 (80) 27 (80)
47 (116) 56 (133)
77 (170) 110 (230)
49 (120) 64 (148)
51 (124) 68 (154)
53 (128) 72 (161)
55 (131) 75 (167)
59 (139) 82 (180)
64 (147) 89 (192)
68 (155) 96 (205)
72 (162) 103 (218)
a
The test pressure of 20,7 MPa ± 3,4 MPa (3 000 psi ± 500 psi) shall be applied as soon as the specimens are placed in the pressure vessel and maintained for the duration of the curing period. The 4 h temperature shall be maintained within ± 2 °C (± 3 °F) throughout the remainder of the curing period and completion of the test.
9.2.3 9.2.3.1
Curing Curing periods
The curing period is the time elapsed from subjecting the specimens to the specified temperature in the curing vessel (or initiating the temperature/pressure schedule in Table 6) to testing the specimen for strength. The strength of the specimen shall be tested at the appropriate time, as specified in Table 7. For specimens cured at atmospheric pressure, the curing period starts when specimens are initially placed in the curing bath preheated to the test temperature. For specimens cured at pressures above atmospheric, the curing period starts with the initial application of pressure and temperature. 9.2.3.2
Specimen cooling
Specimens cured at 60 °C (140 °F) and below shall be removed from the curing bath 45 min ± 5 min before the time at which they will be tested. Specimens shall be removed from their moulds and cooled by being placed in a water bath maintained at 27 °C ± 3 °C (80 °F ± 6 °F) for 40 min. Do not leave the specimen out of water for more than 5 min to avoid dehydration. For specimens cured at temperatures equal to or greater than 77 °C (170 °F), maintain the maximum scheduled temperature and pressure specified in Table 7 until 1 h and 45 min ± 5 min prior to the time at which the specimens will be tested, at which point discontinue heating. During the next 60 min ± 5 min, decrease the temperature to 77 °C (170 °F), or less, without a reduction in the pressure other than that caused by the reduction in temperature. At 45 min ± 5 min prior to the time at which the specimens will be tested, release the pressure remaining and remove the specimens from the moulds. Cool the specimens by transferring them to a water bath maintained at 27 °C ± 3 °C (80 °F ± 6 °F) for 40 min ± 5 min. 9.2.3.3
Specimen acceptance
Cube-test specimens that are damaged shall be discarded prior to testing. If fewer than two test specimens are left for determining the compressive strength at any given period, a retest shall be made.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
20
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
9.3
Test procedure (after ASTM C109/C109M)
9.3.1 Remove specimens from the water bath or the cooling bath that has been maintained at 27 °C ± 3°C (80 °F ± 6 °F). Wipe each specimen to remove any loose material from the faces that will be in contact with the bearing blocks of the testing machine. 9.3.2 The dimensions of the test faces shall be measured to ± 1,0 mm (± 1/16 in) for calculation of the crosssectional area. Apply the load to the specimen faces that were in contact with the plane (vertical) surfaces of the mould (not in contact with the base or the cover plates). Place the specimen in the testing machine centered below the upper bearing block. Prior to the testing of each cube, ascertain that the spherically seated block is free to tilt. Use no cushioning or bedding materials. CAUTION — Employ appropriate safety and handling procedures in testing the specimen. 9.3.3 The rate of loading shall be 72 kN/min ± 7 kN/min (16 000 lbf/min ± 1 600 lbf/min) for specimens expected to have a strength greater than 3,4 MPa (500 psi). For specimens expected to have strength less than 3,4 MPa (500 psi), a 18 kN/min ± 2 kN/min (4 000 lbf/min ± 400 lbf/min) rate shall be used. Depending on the type of compressive strength test machine employed, it can require some time for the load frame to build up the required load rate after initial contact with the cement sample. 9.3.4
9.4
Calculate the compressive strength expressed in megapascals (pounds force per square inch).
Compressive strength acceptance criteria
The compressive strength of all acceptance-test specimens made from the same sample and tested at the same period shall be recorded and averaged to the nearest 50 kPa (10 psi). At least two-thirds of the original individual specimens and the average of all the specimens tested shall meet or exceed the minimum compressive strength specified in Table 7. A retest shall be made if fewer than two strength values are left for determining the compressive strength at any given period.
Cement class
Schedule number
Curing pressureb MPa (psi)
Minimum compressive strength at indicated curing period 8 h ± 15 min MPa (psi)
24 h ± 15 min MPa (psi)
A
—
38 (100)
atm.
1,7 (250)
12,4 (1 800)
B
—
38 (100)
atm.
1,4 (200)
10,3 (1 500)
C
—
38 (100)
atm.
2,1 (300)
13,8 (2 000)
4S
77 (170)
20,7 (3 000)
NRc
6,9 (1 000)
6S
110 (230)
20,7 (3 000)
3,4 (500)
13,8 (2 000)
—
38 (100)
atm.
2,1 (300)
NR
—
60 (140)
atm.
10,3 (1 500)
NR
D
G, H a
Final curing temperaturea °C (°F)
The curing temperature shall be maintained at the indicated temperature ± 2 °C (± 3 °F).
b The test pressure shall be applied as soon as specimens are placed in the pressure vessel, and maintained at the given pressure within ± 3,4 MPa (± 500 psi) for schedules 4S and 6S.
c
NR indicates “no requirement”.
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Table 7 — Compressive strength specification requirements
API SPECIFICATION 10A/ISO 10426-1
21
10 Thickening-time tests 10.1 Apparatus A pressurized consistometer (see Figures 8 and 9) shall consist of a rotating cylindrical slurry container (see Figures 10 and 11) equipped with a stationary paddle assembly (see Figure 12) enclosed in a pressure vessel capable of withstanding the pressures and temperatures described in Tables 9 through 11. The space between the slurry container and the walls of the pressure vessel shall be completely filled with a hydrocarbon oil. The selected oil shall have the following physical properties: ⎯ viscosity range:
6 mm2/s to 79 mm2/s at 38 °C (100 °F) or 6 cSt to 79 cSt at 38 °C (100 °F); or 45 SSU to 360 SSU at 38 °C(100 °F);
⎯ specific heat:
1,9 kJ/(kg⋅K) to 2,5 kJ/(kg⋅K) (0,45 Btu/lb⋅°F to 0,60 Btu/lb⋅°F);
⎯ thermal conductivity:
0,112 W/(m⋅K) to 0,138 W/(m⋅K) [0,065 Btu/(h⋅ft2⋅°F/ft) to 0,08 Btu/(h⋅ft2⋅°F/ft)];
⎯ specific gravity:
0,83 to 0,93.
A heating system capable of raising the temperature of this oil bath at the rate of at least 3 °C/min (6 °F/min) is required. A temperature-measuring system shall be provided for determining and controlling the temperature of the cement slurry (centreline). The slurry container is rotated at a speed of 150 r/min ± 15 r/min. The consistency of the slurry (see 10.2.2.1) shall be measured. The paddle and all parts of the slurry container exposed to the slurry shall be constructed according to the dimensions given in Figures 10 through 12.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
22
Key 1 2 3 4 5 6
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
slurry-container thermocouple sealing ring potentiometer mechanism contact pin pressure port drive bar
7 8 9 10 11 12
wall thermocouple heater cooling coil slurry container container drive table (rotates anticlockwise) removable packing cartridge
13 14 15 16
pressure port thrust bearing mitre gears gear reducer
Figure 8 — Typical gear drive consistometer for pressurized specification thickening-time test
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
23
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
API SPECIFICATION 10A/ISO 10426-1
Key 1 2 3 4 5
slurry-container thermocouple sealing ring potentiometer mechanism contact pin pressure port
6 7 8 9 10
slurry container 11 pressure port cooling coil 12 magnetic drive heater 13 drive belt wall thermocouple container drive table (rotates anticlockwise)
Figure 9 — Typical magnetic drive consistometer for pressurized specification thickening-time tests
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
24
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Dimensions in millimetres (inches) unless otherwise indicated
Key 1 2
temperature measuring device potentiometer mechanism
NOTE
The material is stainless steel, except the diaphragm and the hub.
Figure 10 — Typical slurry container assembly for a pressurized consistometer
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
25
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Dimensions in millimetres (inches)
Key 1 2
diaphragm container base
NOTE
The material is stainless steel, except the diaphragm and the hub.
Figure 11 — Typical slurry container assembly and paddle for a pressurized consistometer
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
26
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Dimensions in millimetres (inches) unless otherwise indicated
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Key 1
trailing edge
2
leading edge
3
paddle shaft
NOTE 1
The paddle material is stainless steel 1,6 mm × 9,5 mm (0,062 5 in × 0,375 in).
NOTE 2
Taper all leading edges out and down, and round all trailing edges.
a b c
Rotate the slurry container table anti-clockwise when viewed from top of paddle. The plane of the top of the paddle brace shall be perpendicular to the shaft at all points of contact. Typical.
Figure 12 — Typical paddle for a pressurized consistometer slurry container
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
27
10.2 Calibration 10.2.1 General Measurement of the thickening time of a cement slurry requires calibration and maintenance of operating systems of the pressurized consistometer including consistency measurement, temperature measuring systems, temperature controllers, motor speed, timer, and gauges. 10.2.2 Consistency 10.2.2.1 Consistency of a cement slurry is expressed in Bearden units of consistency, Bc. This value shall be determined by a potentiometer mechanism and voltage measurement circuit that has been calibrated within one month prior to use, and whenever the calibration spring, resistor or contact arm is adjusted or replaced. The calibration method described in 10.2.2.2 shall be used. 10.2.2.2 A reference weight-loaded device (see Figure 13 for a typical potentiometer calibrating device and Figure 14 for a typical potentiometer mechanism) is used to produce a series of torque equivalent values for consistency for calibration. Reference weights are used to apply torque to the potentiometer spring, using the radius of the potentiometer frame as a lever arm. As reference weights are added, the spring is deflected and resulting DC voltage and/or Bc increases. See Table 8. NOTE
See manufacturer's instruction manual for procedures.
The calibrated torque-equivalent values, T, expressed in gram centimetres, are defined by Equation (2): T = 78,2 + 20,02Bc
(2)
where Bc is the consistency, expressed in Bearden units.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Table 8 — Slurry consistency vs. equivalent torque (for a potentiometera mechanism with a radius of 52 mm ±1 mm) Torque equivalent
Mass of reference weights
Slurry consistency
g⋅cm
g ± 0,1 g
Bc ±5
260
50
9
520
100
22
780
150
35
1 040
200
48
1 300
250
61
1 560
300
74
1 820
350
87
2 080
400
100
a For a potentiometer mechanism with a different radius, an appropriate table with equivalent tolerances shall be used.
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
28
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Figure 13 — Typical potentiometer calibrating device
Key 1 resistor 2 bearing shaft 3 arm contact 4 collar, spring 5 sleeve, spring
6 7 8 9 10
retainer, shaft bearing spring clamp, spring adjustor insulator adjustor, spring resistor
11 12 13 14 15
frame, mount stop, mount frame contact springs bearing, frame arm, stop
Figure 14 — Typical potentiometer mechanism for a pressurized consistometer --`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
29
10.2.3 Temperature-measuring system The temperature-measuring system shall be calibrated to an accuracy of ± 2 °C (± 3 °F). Calibration shall be no less frequently than quarterly. The procedure described in Annex A is commonly used. 10.2.4 Motor speed The motor shall rotate the slurry container at 150 r/min ± 15 r/min (2,5 r/s ± 0,25 r/s) and shall be checked annually. 10.2.5 Timer Timers shall be accurate to within ± 30 s per hour and shall be checked annually. 10.2.6 Pressure-measuring system Calibration shall be conducted annually against a dead-weight tester or master gauge. Gauges shall be calibrated at 17 MPa, 34 MPa, and 52 Mpa ± 1,7 MPa (2 500 psi, 5 000 psi, and 7 500 psi ± 250 psi).
10.3 Procedure 10.3.1 Operating instructions --`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Detailed operating instructions developed by the operator, or furnished by the equipment manufacturer, are applicable for this method and shall be followed, provided they conform to the specifications contained in this part of ISO 10426. Grease may be placed only on the threaded surfaces of the slurry container. 10.3.2 Filling of slurry container 10.3.2.1
Pour the slurry (prepared in accordance with Clause 7) into the inverted slurry container.
NOTE Slurry segregation can occur during the filling operation. This can be reduced by stirring the slurry in the mixing container with a spatula while pouring. Segregation is less of a problem when the time from cessation of mixing to completing the filling operation is kept to a minimum.
10.3.2.2 When the slurry container is full, strike the outside of the container and remove air that rises to the top of the slurry. 10.3.2.3
Then, secure the slurry container base in place.
10.3.2.4
Then, secure the centre plug (pivot bearing) into the container base.
10.3.3 Initiation of test 10.3.3.1 Place the slurry container on the drive table in the pressure vessel, start rotation of the slurry container, place the potentiometer mechanism so as to engage the shaft drive bar, and begin filling the vessel with oil. 10.3.3.2 Close the head assembly of the pressure vessel securely, insert the thermocouple, and partially engage its threads. 10.3.3.3
After the pressure vessel is completely filled with oil, tighten the threads of the thermocouple.
10.3.3.4
Initiate the test by applying pressure and temperature within 5 min after cessation of mixing.
10.3.4 Temperature and pressure control During the test period, increase the temperature and pressure of the cement slurry in the slurry container in accordance with the appropriate specification schedule given in Table 9, Table 10, or Table 11. During the pressure and temperature ramp of schedules 4, 5 and 6, the temperature and pressure shall be maintained within ± 3 °C (± 6 °F) and ± 2 MPa (± 300 psi), respectively, of the appropriate elapsed time versus temperature and pressure target. Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
30
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
Within 10 min after the end of the ramp, the temperature and pressure shall be within ± 1 °C (± 2 °F) and ± 0,7 MPa (± 100 psi), respectively, of the specified values. Determine the temperature of the cement slurry for specification testing by the use of a temperature-measuring device located in the centre of the sample container. The tip of the thermocouple shall be vertically positioned within the paddle shaft in the slurry cup in such a way that it is between 45 mm (1,77 in) and 89 mm (3,5 in) above the inside of the base of the sample container. As there are many models of consistometers having different dimensions, care shall be taken to ensure that the thermocouple used is compatible with the consistometer and that the position of the tip of the thermocouple is in the correct location specified above. Table 9 — Schedule 4 specification thickening-time test for classes A, B, C and D cement Elapsed time min
Pressure MPa (psi)
Temperature °C (°F)
0
5,2 (750)
27 (80)
2
7,6 (1 100)
28 (83)
4
9,7 (1 400)
31 (87)
6
11,7 (1 700)
32 (90)
8
13,8 (2 000)
34 (93)
10
15,9 (2 300)
36 (97)
12
17,9 (2 600)
38 (100)
14
20,0 (2 900)
39 (103)
16
22,1 (3 200)
41 (106)
18
24,8 (3 600)
43 (110)
20
26,7 (3 870)
45 (113)
Table 10 — Schedule 5 specification thickening-time test for classes G and H cement
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Elapsed time min
Pressure MPa (psi)
Temperature °C (°F)
0
6,9 (1 000)
27 (80)
2
9,0 (1 300)
28 (83)
4
11,1 (1 600)
30 (86)
6
13,1 (1 900)
32 (90)
8
15,2 (2 200)
34 (93)
10
17,3 (2 500)
36 (96)
12
19,3 (2 800)
37 (99)
14
21,4 (3 100)
39 (102)
16
23,4 (3 400)
41 (106)
18
25,5 (3 700)
43 (109)
20
27,6 (4 000)
44 (112)
22
29,6 (4 300)
46 (115)
24
31,7 (4 600)
48 (119)
26
33,8 (4 900)
50 (122)
28
35,6 (5 160)
52 (125)
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
API SPECIFICATION 10A/ISO 10426-1
31
Table 11 — Schedule 6 specification thickening-time test for Class D cement Elapsed time min
Pressure MPa (psi)
Temperature °C (°F)
0 2 4 6 8 10 12 14 16 18 20 22 24 26 28 30 32 34 36
8,6 (1 250) 11,0 (1 600) 13,1 (1 900) 15,9 (2 300) 17,9 (2 600) 20,7 (3 000) 22,8 (3 300) 25,5 (3 700) 27,6 (4 000) 30,3 (4 400) 32,4 (4 700) 35,2 (5 100) 37,2 (5 400) 39,3 (5 700) 42,1 (6 100) 44,1 (6 400) 46,9 (6 800) 49,0 (7 100) 51,6 (7 480)
27 (80) 29 (84) 31 (87) 33 (91) 34 (94) 37 (98) 38 (101) 41 (105) 42 (108) 44 (112) 47 (116) 48 (119) 51 (123) 52 (126) 54 (130) 56 (133) 58 (137) 60 (140) 62 (144)
10.4 Thickening time and consistency Record the elapsed time between the initial application of pressure and temperature (initiation of the test) to the pressurized consistometer and the time at which a consistency of 100 Bc is reached, as the thickening time for the test. Report the maximum consistency during the 15 min to 30 min period after the initiation of the test.
10.5 Specification acceptance requirements The acceptance requirements for the maximum consistency during the 15 min to 30 min period after the initiation of the test shall be 30 Bc for all classes of cement manufactured in accordance with this part of ISO 10426. The acceptance requirement for the thickening time shall be in accordance with Table 12. Table 12 — Thickening time acceptance requirement Class
Schedule
Minimum thickening time min
Maximum thickening time min
A
4
90
NRa
B
4
90
NR
C
4
90
NR
4
90
NR
6
100
NR
G
5
90
120
H
5
90
120
D
a
NR indicates “no requirement.” --`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
32
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
11 Marking The following information shall be marked on or made available with each shipment of well cement. For sacked cement, the information required shall be marked on each sack; for bulk cement, the information required shall be marked or attached to the bill of lading on each shipment: a)
manufacturer's name;
b)
class and sulfate-resistance grade of cement;
c)
net mass.
12 Packing Well cement shall be furnished in bulk or in sacks. Each sack shall contain a specified net mass of ± 2 %. The average net mass of 5 % of all sacks in a shipment, taken at random, shall not be less than the specified mass. A cement sack should be resistant to moisture, resistant to damage during handling and easy to cut during transfer to bulk facilities. Cement sacks should typically consist of up to six paper layers with a minimum areic mass of 70 g/m2 (0.014 lbm/ft2) each with up to two polyethylene or polypropylene layers with an areic mass of 15 g/m2 (0.003 lbm/ft2) to 24 g/m2 (0.005 lbm/ft2) each included between the first and fifth paper layers. Up to two asphalt or bitumen layers may be included to further improve resistance to damage. Flexible bulk cement containers should provide an acceptable tensile strength (safety factor 5 to 1 minimum). They should also be resistant to ultraviolet radiation when polyethylene or polypropylene layers are used and be suitably moisture-proof.
13 Bentonite Bentonite is a naturally occurring clay mineral, composed primarily of smectite. Non-treated bentonite, for use in well cementing, is dried and ground, but not chemically treated during processing. Bentonite meeting the requirements of this part of ISO 10426 for use in well cementing shall meet all the requirements for non-treated bentonite in accordance with ISO 13500. Table 13 — Bentonite acceptance requirements Specification
Yield point/plastic viscosity ratio
1,5 maximum
Dispersed plastic viscosity
10 cP minimum
Dispersed filtrate volume
12,5 ml maximum
See ISO 13500 for test procedures.
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
NOTE
Requirement
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
Annex A (informative) Calibration procedures for thermocouples, temperature measuring systems, and controllers
A.1 Calibration methods There are several satisfactory methods for calibrating thermocouples, including methods supplied by equipment manufacturers. See ASTM E220 for a more complete discussion of these procedures. No ASTM procedures for calibration of temperature measuring systems are available.
A.2 Thermocouple calibration A.2.1 Apparatus A.2.1.1
General
The individual pieces of apparatus required to carry out the calibration depend on the particular technique selected. Those features that need special attention, regardless of the technique, are highlighted in A.2.1.2 to A.2.1.4. A.2.1.2
Heating environment
A.2.1.3
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
The heating medium should permit proper immersion of both the test thermocouple (the one being calibrated) and the reference thermocouple or reference thermometer. The apparatus should be capable of maintaining a stable temperature that is uniform throughout the test section. Temperature measurement
The reference temperature of the heating medium may be measured by using either a thermometer or a thermocouple. The accuracy of the reference measuring device should be traceable to the reference of the national body responsible for standards of temperature measurement, for example the NBS certification in the USA. A.2.1.4
Thermocouple voltage output
If a thermocouple is used to sense the reference temperature, the voltage output from the reference thermocouple and test thermocouple should be determined as described in applicable national standards, such as ASTM E220. In this case, tables of temperature vs. voltage for the type of thermocouple being used should be consulted to determine the temperature. Alternatively, a direct-reading, temperature-compensated readout instrument may be used. The accuracy of the instrument should be traceable to national standards certification.
A.2.2 Procedure A.2.2.1 With the exception of the indicating instruments, the specific procedures are detailed in applicable national standards, such as ASTM E220. The items in A.2.2.2 through A.2.2.6 require special attention or are related to the use of the indicating type of equipment. A.2.2.2 The test and reference thermocouples or thermometers should be placed as close together as possible in the heating medium. Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for33 Resale, 02/05/2017 10:04:43 MST
34
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
A.2.2.3 After each change in heating level, the temperature should be allowed to remain at a stable value for 15 min before reading the reference temperature (or voltage) and the test thermocouple temperature (or voltage). A.2.2.4 Several (more than three) test temperatures that span the operating range of the equipment should be used in the calibration procedure. A.2.2.5 If the test thermocouple does not accurately sense the temperature, a calibration curve should be drawn and used to correct the indicated temperatures from the test thermocouple. Occasionally, small inaccuracies in thermocouple response can be compensated for during the calibration of the temperature measuring system being used in conjunction with the thermocouple (see A.3). A.2.2.6 If the test thermocouple error is greater than that specified by the manufacturer, the thermocouple should be replaced by one that meets the thermocouple accuracy limits. The ASTM E220 classification “special” type J thermocouple has error limits equal to or better than ± 1 °C (± 2 °F) up to 277 °C (530 °F).
A.3 Calibration of temperature measuring systems and controllers A.3.1 Apparatus The calibration of temperature-measuring systems and controllers requires a millivolt source, the correct connecting thermocouple extension cable for the type of thermocouple being used and, possibly, a thermometer and a table of reference voltages. Signal sources, or calibrators, are of two types, namely, uncompensated and cold-junction-compensated. Several commercial calibrators are available that are cold-junction-compensated and have a digital display of the temperature equivalent to the millivolt signal being supplied. The accuracy of all calibration apparatus should be traceable to national-standards certification. Some older galvanometer-type temperature-indicating instruments and controllers require a stronger signal for operation than the newer potentiometric and digital-type temperature measuring systems and controllers and, therefore, require a calibrator with sufficient signal strength to give an accurate calibration.
A.3.2 Procedure
A.3.2.2 The thermocouple extension cable should be fitted with a proper thermocouple grade adapter to permit plugging it into the same receptacle used for connecting the test equipment thermocouple. Care should be taken to ensure the correct polarity of the connections. Calibrators, temperature-measuring systems, and controllers should be allowed proper warm-up time, as specified by the manufacturer, for greatest accuracy. A.3.2.3 It is only necessary that thermocouple calibrators with cold-junction compensation be properly connected with the proper thermocouple extension cable and thermocouple connectors. The temperaturemeasuring systems and/or controllers using this signal should have the same temperature readout, within the accuracy of the temperature or controllers as supplied by the manufacturer. A.3.2.4 Uncompensated thermocouple calibrators require a thermometer to determine the cold-junction temperature of the thermocouple extension cable connection of the calibrator. This cold-junction temperature is set on the calibrator by the operator. A.3.2.5 The use of an uncompensated millivolt potentiometer requires that the temperature at the calibrator/thermocouple extension cable terminals be read with a thermometer of known accuracy. The millivolt equivalent of this temperature is then subtracted from the equivalent test millivolt signal to obtain the calibrator millivolt signal used. These voltages may be found in reference mV/temperature tables for the type of thermocouple in use.
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
A.3.2.1 The manufacturer's procedure for calibrating temperature-measuring systems and controllers should be followed. The items in A.3.2.2 to A.3.2.5 require special attention.
Annex B (informative) Use of the API Monogram by Licensees
B.1
Scope
The API Monogram Program allows an API Licensee to apply the API Monogram to products. The API Monogram Program delivers significant value to the international oil and gas industry by linking the verification of an organization's quality management system with the demonstrated ability to meet specific product specification requirements. The use of the Monogram on products constitutes a representation and warranty by the Licensee to purchasers of the products that, on the date indicated, the products were produced in accordance with a verified quality management system and in accordance with an API product specification. When used in conjunction with the requirements of the API License Agreement, API Spec Q1, in its entirety, defines the requirements for those organizations who wish to voluntarily obtain an API license to provide API monogrammed products in accordance with an API product specification. API Monogram Program licenses are issued only after an on-site audit has verified that the Licensee conforms to the requirements described in API Spec Q1 in total, and the requirements of an API product specification. Customers/users are requested to report to API all problems with API monogrammed products. The effectiveness of the API Monogram Program can be strengthened by customers/users reporting problems encountered with API monogrammed products. A nonconformance may be reported using the API Nonconformance Reporting System available at http://compositelist.api.org/ncr.asp. API solicits information on new product that is found to be nonconforming with API specified requirements, as well as field failures (or malfunctions), which are judged to be caused by either specification deficiencies or nonconformities with API specified requirements. This annex sets forth the API Monogram Program requirements necessary for a supplier to consistently produce products in accordance with API specified requirements. For information on becoming an API Monogram Licensee, please contact API, Certification Programs, 1220 L Street, N. W., Washington, D.C. 20005 or call 202962-4791 or by email at
[email protected].
B.2
References
In addition to the referenced standards listed earlier in this document, this annex references the following standard: API Specification Q1. For Licensees under the Monogram Program, the latest version of this document shall be used. The requirements identified therein are mandatory.
B.3
API Monogram Program: Licensee Responsibilities
B.3.1 Maintaining a License to Use the API Monogram For all organizations desiring to acquire and maintain a license to use the API Monogram, conformance with the following shall be required at all times: a)
the quality management system requirements of API Spec Q1;
b)
the API Monogram Program requirements of API Spec Q1, Annex A;
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for35 Resale, 02/05/2017 10:04:43 MST
36
CEMENTS AND MATERIALS FOR WELL CEMENTING—PART 1: SPECIFICATION
c)
the requirements contained in the API product specification(s) for which the organization desires to be licensed;
d)
the requirements contained in the API Monogram Program License Agreement.
B.3.2 Monogrammed Product — Conformance with API Spec Q1 When an API-licensed organization is providing an API monogrammed product, conformance with API specified requirements, described in API Spec Q1, including Annex A, is required.
B.3.3 Application of the API Monogram
a)
Each Licensee shall develop and maintain an API Monogram marking procedure that documents the marking/monogramming requirements specified by the API product specification to be used for application of the API Monogram by the Licensee. The marking procedure shall define the location(s) where the Licensee shall apply the API Monogram and require that the Licensee's license number and date of manufacture be marked on monogrammed products in conjunction with the API Monogram. At a minimum, the date of manufacture shall be two digits representing the month and two digits representing the year (e.g. 05-07 for May 2007) unless otherwise stipulated in the applicable API product specification. Where there are no API product specification marking requirements, the Licensee shall define the location(s) where this information is applied.
b)
The API Monogram may be applied at any time appropriate during the production process but shall be removed in accordance with the Licensee’s API Monogram marking procedure if the product is subsequently found to be nonconforming with API specified requirements. Products that do not conform to API specified requirements shall not bear the API Monogram.
c)
Only an API Licensee may apply the API Monogram and its license number to API monogrammable products. For certain manufacturing processes or types of products, alternative API Monogram marking procedures may be acceptable. The current API requirements for Monogram marking are detailed in the API Policy Document, Monogram Marking Requirements, available on the API Monogram Program website at http://www.api.org/certifications/monogram/.
d)
The API Monogram shall be applied at the licensed facility.
e)
The authority responsible for applying and removing the API Monogram shall be defined in the Licensee’s API Monogram marking procedure.
B.3.4 Records Records required by API product specifications shall be retained for a minimum of five years or for the period of time specified within the product specification if greater than five years. Records specified to demonstrate achievement of the effective operation of the quality system shall be maintained for a minimum of five years.
B.3.5 Quality Program Changes Any proposed change to the Licensee’s quality program to a degree requiring changes to the quality manual shall be submitted to API for acceptance prior to incorporation into the Licensee's quality program.
B.3.6 Use of the API Monogram in Advertising Licensee shall not use the API Monogram on letterheads or in any advertising (including company-sponsored web sites) without an express statement of fact describing the scope of Licensee’s authorization (license number). The Licensee should contact API for guidance on the use of the API Monogram other than on products. Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Each Licensee shall control the application of the API Monogram in accordance with the following.
API SPECIFICATION 10A/ISO 10426-1
B.4
37
Marking Requirements for Products
These marking requirements apply only to those API Licensees wishing to mark their products with the API Monogram.
B.4.1 Product Specification Identification Manufacturers shall mark or make available the information identified in Section 11, as a minimum, including “API Spec 10A.”
B.4.2 Units As a minimum, product should be marked with U.S. customary (USC) units. Use of dual units [metric (SI) units and USC units] is acceptable.
B.4.3 Markings For sacked cement, the information required shall be marked on each sack. For bulk cement, the information required shall be marked or attached to the bill of lading on each shipment. The following information is required at minimum: a)
API Spec 10A;
b)
net mass (in U.S. customary (USC) units);
c)
class and sufate-resistance grade of cement.
The complete API monogram marking consists of the following: ⎯ the letters “Spec 10A,” ⎯ the manufacturer’s API license number, ⎯ the API monogram, ⎯ the date of manufacture (defined as the month and year when the monogram is applied by the manufacturer).
B.4.4 License Number The API Monogram license number shall not be used unless it is marked in conjunction with the API Monogram.
B.5
API Monogram Program: API Responsibilities
The API shall maintain records of reported problems encountered with API monogrammed products. Documented cases of nonconformity with API specified requirements may be reason for an audit of the Licensee involved, (also known as audit for “cause”). Documented cases of specification deficiencies shall be reported, without reference to Licensees, customers or users, to API Subcommittee 18 (Quality) and to the applicable API Standards Subcommittee for corrective actions.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
Bibliography
ASTM C150, Standard Specification for Portland Cement
[2]
ASTM E220, Standard Test Method for Calibration of Thermocouples by Comparison Techniques
[3]
ASTM C114, Standard Test Methods for Chemical Analysis of Hydraulic Cement
[4]
ASTM C183, Standard Practice for Sampling and the Amount of Testing of Hydraulic Cement
[5]
ASTM C204, Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus
[6]
ASTM E11, Standard Specification for Wire Cloth and Sieves for Testing Purposes
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
[1]
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
2010 PUBLICATIONS ORDER FORM Effective January 1, 2010. API Members receive a 30% discount where applicable. The member discount does not apply to purchases made for the purpose of resale or for incorporation into commercial products, training courses, workshops, or other commercial enterprises. Online: www.api.org/pubs Phone: 1-800-854-7179 (Toll-free in the U.S. and Canada) | (+1) 303-397-7956 (Local and International) Fax: (+1) 303-397-2740
Date:
❏ API Member (Check if Yes)
Invoice To (❏ Check here if same as “Ship To”)
Ship To (UPS will not deliver to a P.O. Box)
Name:
Name:
Title:
Title:
Company:
Company:
Department:
Department:
Address:
Address:
City:
State/Province:
City:
State/Province:
Zip/Postal Code:
Country:
Zip/Postal Code:
Country:
Telephone:
Telephone:
Fax:
Fax:
Email:
Email:
Quantity
Title
SO★
Unit Price
RP 10B-2, Testing Well Cements
$205.00
RP 10B-3, Testing of Deepwater Well Cement Formulations
$74.00
RP 10B-4, Preparation and Testing of Foamed Cement Slurries at Atmospheric Pressure
$74.00
RP 10B-5, Determination of Shrinkage and Expansion of Well Cement Formulations at Atmospheric Pressure
$77.00
RP 10B-6, Determining the Static Gel Strength of Cement Formulations
$60.00
❏ Payment Enclosed ❏ P.O. No. (Enclose Copy) ❏ Charge My IHS Account No. ❏ VISA ❏ MasterCard ❏ American Express ❏ Diners Club ❏ Discover Credit Card No.: Print Name (As It Appears on Card): Expiration Date: Signature:
Total
Subtotal Applicable Sales Tax (see below) Rush Shipping Fee (see below) Shipping and Handling (see below) Total (in U.S. Dollars) ★ To be placed on Standing Order for future editions of this publication, place a check mark in the SO column and sign here:
Pricing and availability subject to change without notice.
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Ordering Information
Mail Orders – Payment by check or money order in U.S. dollars is required except for established accounts. State and local taxes, $10 processing fee, and 5% shipping must be added. Send mail orders to: API Publications, IHS, 15 Inverness Way East, c/o Retail Sales, Englewood, CO 80112-5776, USA. Purchase Orders – Purchase orders are accepted from established accounts. Invoice will include actual freight cost, a $10 processing fee, plus state and local taxes. Telephone Orders – If ordering by telephone, a $10 processing fee and actual freight costs will be added to the order. Sales Tax – All U.S. purchases must include applicable state and local sales tax. Customers claiming tax-exempt status must provide IHS with a copy of their exemption certificate. Shipping (U.S. Orders) – Orders shipped within the U.S. are sent via traceable means. Most orders are shipped the same day. Subscription updates are sent by First-Class Mail. Other options, including next-day service, air service, and fax transmission are available at additional cost. Call 1-800-854-7179 for more information. Shipping (International Orders) – Standard international shipping is by air express courier service. Subscription updates are sent by World Mail. Normal delivery is 3-4 days from shipping date. Rush Shipping Fee – Next Day Delivery orders charge is $20 in addition to the carrier charges. Next Day Delivery orders must be placed by 2:00 p.m. MST to ensure overnight delivery. Returns – All returns must be pre-approved by calling the IHS Customer Service Department at 1-800-624-3974 for information and assistance. There may be a 15% restocking fee. Special order items, electronic documents, and age-dated materials are non-returnable. Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
THERE’S MORE WHERE THIS CAME FROM. API Monogram® Licensing Program Sales: (+1) 713-964-2662 Service: (+1) 202-962-4791 Fax: (+1) 202-682-8070 Email:
[email protected] Web: www.api.org/monogram API Quality Registrar (APIQR®) • ISO 9001 • ISO/TS 29001 • ISO 14001 • OHSAS 18001 • API Spec Q1® • API QualityPlus® • Dual Registration Sales: (+1) 713-964-2662 Service: (+1) 202-962-4791 Fax: (+1) 202-682-8070 Email:
[email protected] Web: www.api.org/apiqr
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
API Individual Certification Programs (ICP®) Sales: (+1) 713-964-2662 Service: (+1) 202-682-8064 Fax: (+1) 202-682-8348 Email:
[email protected] Web: www.api.org/icp API Engine Oil Licensing and Certification System (EOLCS) Sales: (+1) 713-964-2662 Service: (+1) 202-682-8516 Fax: (+1) 202-962-4739 Email:
[email protected] Web: www.api.org/eolcs
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
API Training Provider Certification Program (API TPCP™) Sales: (+1) 713-964-2662 Service: (+1) 202-682-8075 Fax: (+1) 202-682-8070 Email:
[email protected] Web: www.api.org/tpcp API Perforator Design Registration Program Sales: (+1) 713-964-2662 Service: (+1) 202-682-8490 Fax: (+1) 202-682-8070 Email:
[email protected] Web: www.api.org/perforators API Credit Exchange (ACE™) Service: (+1) 202-682-8192 Fax: (+1) 202-682-8070 Email:
[email protected] Web: www.api.org/ace API Diesel Exhaust Fluid Certification Program Phone: (+1) 202-682-8516 Fax: (+1) 202-962-4739 Email:
[email protected] Web: www.apidef.org API WorkSafe™ Sales: (+1) 713-964-2662 Service: (+1) 202-682-8469 Fax: (+1) 202-682-8348 Email:
[email protected] Web: www.api.org/worksafe
API-U Phone: Fax: Email: Web:
(+1) 202-682-8053 (+1) 202-682-8070
[email protected] www.api-u.org
API Data™ Phone: (+1) 202-682-8499 Fax: (+1) 202-962-4730 Email:
[email protected] Web: www.APIDataNow.org API Publications Online: www.api.org/pubs Phone: 1-800-854-7179 (Toll-free: U.S./Canada) (+1) 303-397-7956 (Local/International) Fax: (+1) 303-397-2740 API Standards Phone: (+1) 202-682-8148 Fax: (+1) 202-962-4797 Email: standards.org Web: www.api.org/standards
Request a Quotation: www.api.org/quote
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST
--`,,,,``,,`,,``,`````,,`,,`,,,,-`-`,,`,,`,`,,`---
Product No. GX10A24
Copyright American Petroleum Institute Provided by IHS under license with API No reproduction or networking permitted without license from IHS
Licensee=Baker Hughes - Operation Sites/5368601001, User=Arroyo, Jorge Not for Resale, 02/05/2017 10:04:43 MST